| Laboratory Test Sheet |
| ANALYSIS OF BITUMINOUS MATERIALS BS 598 : PART 102 : 1989 |
| Method 4.1 / Method 4.2 - Filler Direct / Difference* |
| Site : |
| Client : |
| Client Ref. : |
| Job No. : |
| Date Received : |
| Lab. Ref. : |
| Supplier : |
| Source : |
| Specification : |
| Material Type : |
| Binder Type/Grade : |
| Aggregate Type : |
| Specified |
| Actual |
| Time Off |
| Time On |
| Tray No. : |
| Weight of Sample (M) : |
| not > 4 hrs. |
| Reheating Time (min.) (See BS 598 : Part 101 : 1987) |
| Reheating Temperature(°c) (See BS 598 : Part 101 : 1987) |
| Volume of Solvent (V) : |
| Volume of Aliquot (v) : |
| Time On |
| Actual |
| Time Off |
| Specified |
| (°c) |
| Temperature of Solvent (t1) : |
| Rolling Time (BS 598 : Part 102 : 1989 : Table 3) |
| Centrifuging Time (BS 598 : Part 102 : 1989 : Figure 2) |
| Temperature of Solvent (t2) : |
| (°c) |
| (Difference between t1 and t2 must not be >3°c) |
| Flask Ref.: |
| Weight of Flask : |
| (g) |
| (g) |
| Weight of Flask & Recovered Binder : |
| (g) |
| (g) |
| Weight of Binder (0.75 - 1.25g ) Difference must not be greater than 0.02g |
| (g) |
| (g) |
| Soluble Binder Content (s) |
| 10000 z V |
| (%) |
| (g) |
| Average Weight of Binder |
| v M (100-P) (1-z/dv) |
| (g) |
| Weight of Recovered Aggregate (M3) : |
| 1 |
| Max. Wt. |
| Weight Retained (g) |
| % Retained |
| % Passing |
| Specification % Passing |
| BS Sieve |
| Rep.% Passing |
| 50 mm |
| 5000 g |
| 37.5 mm |
| 4000 g |
| 3000 g |
| 28 mm |
| 20 mm |
| 2500 g |
| 2000 g |
| 14 mm |
| 10 mm |
| 1500 g |
| 1000 g |
| 6.3 mm |
| 2 |
| 3.35 mm |
| 550 g |
| 2 |
| 450 g |
| 2.36 mm |
| Riffle Weight passing BS sieve |
| mm = |
| Weight after Riffle = |
| Riffle Factor = |
| 1.18 mm |
| 125 g |
| 600 µm |
| 100 g |
| 425 µm |
| 80 g |
| 300 µm |
| 65 g |
| 212 µm |
| 60 g |
| 50 g |
| 150 µm |
| 30 g |
| 75 µm |
| Pan |
| Filler |
| 3 |
| TOTALS |
| (%) |
| Mid-Point Specified Grading on 2.36/3.35* mm Test Sieve |
| (%) |
| Deviation of Grading from Mid-Point of 2.36/3.35* mm Test Sieve |
| Found |
| Correction |
| Corrected |
| Spec. Limits |
| Aggregate Passing 75 µm Test Sieve (%) |
| Soluble Binder (%) |
| Comments : |
| Date : |
| Tested By : |
| Checked By : |
| Date : |
| Check Level (1 / 2 / 3)* |
| Notes : * - Delete as applicable 1 - For 300 mm dia. down to 2.36 mm aperature and thereafter 200 mm dia. |
| 2 - Use this value to obtain correction figures 3 - Must equal mass of Recovered Aggregate M3 |