Laboratory Test Sheet  
   
Analysis of Bituminous Materials  BS 598 Part 102 1989
Method 4.1 / Method 4.2 - Filler Direct / Difference*  
   
Client : Site  
Client Ref. : Lab Ref Job No  
Supplier : Source  
Material Type : Specification  
Aggregate Type  Binder Type  
   
   
Weight of Sample (M) : Tray   Specified Time on Time off Actual
Reheating Time (min.) (See BS 598 : Part 101 : 1987)
  
Reheating Temperature(°c) (See BS 598 : Part 101 : 1987)
Volume of Solvent (V) : Volume of Aliquot (v) :
Temperature of Solvent (t1) :
 Specified Time on Time off Actual
Rolling Time (BS 598 : Part 102 : 1989 : Table 3)
Centrifuging Time (BS 598 : Part 102 : 1989 : Figure 2)
Temperature of Solvent (t2) :
(Difference between t1 and t2 must not be >3°c)
  
Flask Ref.:  
Weight of Flask :  
Weight of Flask & Recovered Binder :  
Weight of Binder (0.75 - 1.25g ) Difference must not be greater than 0.02g
  
Average Weight of Binder  10000 z V  
Weight of Recovered Aggregate (M3) :
v M (100-P) (1-z/dv)
  
BS Sieve Max Wt Wt Retained (g) % Retd %Pass Rep % Passing Spec
50 mm 5000 g
37.5 mm 4000 g
28 mm 3000 g
20 mm 2500 g
14 mm 2000 g
10 mm 1500 g
6.3 mm 1000 g
3.35 mm 550 g
2.36 mm 450 g
Riffle weight passing BS Sieve mm Wt after riffling Riffle Factor
1.18 mm 125 g
600 um 100 g
425 mm 80 g
300 um 65 g
150 um 60 g
75 um 30 g
Pan
Filler
Totals
Mid-Point Specified Grading on 2.36/3.35* mm Test Sieve
 %  
Deviation of Grading from Mid-Point of 2.36/3.35* mm Test Sieve             %      
Found Correction Corrected Spec Limit
Aggregate Passing 75 µm Test Sieve %            
Soluble Binder
                     
Comments :                    
Tested By :    
Date :
 Checked by   Date:
           
Check Level (1 / 2 / 3)*
        
                     
Notes :  * Delete as applicable                                        1  For 300 mm dia. down to 2.36 mm aperature and thereafter 200 mm dia.                    
 2  Use this value to obtain correction figures                    3 Must equal mass of  Recovered Aggregate M3